主講人 : Tadashi Furuhara
Recent advances in high-strength steels for automobile applications or surface-hardened steels have attracted interest on controlling the nanoscale dispersion of alloy carbides/nitrides in ferrite. Particularly, B1-type carbide/nitride precipitation and stable alloy clustering can be understood as the coupled ordering and compositional phase separation of interstitial alloying elements "i" and substitutional alloying elements "s". In this presentation, the behaviour of i–s clustering and alloy carbide/nitride precipitation is introduced d on nanoscale characterization, theoretical calculations, and evaluations of mechanical properties. It is shown that strong i–s attractive interaction is responsible for stable i–s clustering, which clearly indicates "hidden" nanoscale inhomogeneity in solid solutions. Further, we discuss a concept termed interstitial sublattice engineering in bulk and at interphase boundary for designing high strength steels.
主講人簡介：
Tadashi Furuhara，教授，博士生導師，日本東北大學材料研究所所長、教授。先后獲日本京都大學碩士學位，美國卡內基梅隆大學博士學位。曾任日本京都大學助理教授和副教授，2005年晉升為日本東北大學教授。主要研究領域包括鋼鐵和有色金屬的物理冶金學，如相變/析出、形變/再結晶、基于熱機械/熱化學方法的微觀組織控制。已在國際學術刊物上發表了256篇研究論文，91篇國際會議論文，62篇綜述文章，合著了16本書，論文引用次數13256次，H-因子 60，獲獎26次/個，包括英國礦業協會 Vandium Award(2022),國際相變學會Hillert-Cahn Award（2022）,日本金屬與材料學會Excellent microscopy award （2021），日本金屬材料研究所谷川哈里斯獎（2015年）、日本鈦學會技術獎（2006年）、日本鋼鐵研究所西山紀念獎（2000年）等多項獎項。
Tadashi Furuhara教授積極為冶金領域各學術團體作出貢獻，曾是日本金屬學會副會長和日本鐵鋼協會副會長，且一直是礦物、金屬和材料學會（TMS）相變委員會和鋼鐵委員會成員，目前擔任Acta Materialia和 a Materialia編輯。國際相變委員會、鋼鐵協會、美國TMS委員，日本東北大學金屬材料研究所所長，日本鋼鐵協會會長。
編輯：曹蔚
責編：韋麗